超级双相不锈钢中δ相力学性能的纳米压痕表征
姚瑶;周灿栋;史弼;杨晓萍;单爱党;宋洪伟
【期刊名称】《机械工程材料》 【年(卷),期】2011(035)007
【摘要】To predict the effect of a phase precipitation on mechanical properties of 00Cr25Ni7Mo4N super duplex stainless steel, the intermetallics a phase was characterized by nanoindentation after slow cooling, and the microstructure was observed. The results show that the volume fraction of δ phase in the steel was 36. 7%, and the nanoindentation hardness of the δ phase was in the range of 14. 0-17. 1 GPa with a mean value of 15.7 GPa; the modulus of elasticity was in the range of 262-380 GPa with a mean value of 317 GPa. In addition, the substrateeffect on results could be removed.%为了预测金属间化合物d相的析出对00Cr25Ni7M04N超级双相不锈钢力学性能的影响，采用纳米压痕技术对加热缓冷后该钢的δ相进行了表征，并对其显微组织进行了观察。结果表明：钢中d相的体积分数为36．7％，其纳米压痕硬度范围为14．0～17．1GPa，平均值为15．7GPa，弹性模量范围为262~380GPa，平均值为317GPa；测试结果基本排除了基体效应的影响。 【总页数】4页(1-3,7)
【关键词】双相不锈钢;δ相;力学性能;纳米压痕 【作者】姚瑶;周灿栋;史弼;杨晓萍;单爱党;宋洪伟
【作者单位】上海交通大学材料科学与工程学院,上海200240;宝钢股份有限公
司研究院,上海201900;宝钢股份有限公司研究院,上海201900;宝钢股份有限公司研究院,上海201900;上海交通大学材料科学与工程学院,上海200240;宝钢股份有限公司研究院,上海201900 【正文语种】中文 【中图分类】TG142.1 【相关文献】
1.跟踪国际潮流，推广使用耐蚀性能更好、力学性能更高的双相不锈钢——2006年第二届北京国际双相不锈钢大会圆满结束 [J],
2.时效工艺对2205双相不锈钢组织与力学性能的影响 [J], 王佳; 张骞
3.稀土元素对2205双相不锈钢组织与力学性能的影响 [J], 刘晓; 陈雷; 杜晓建; 王龙妹
4.镧铈混合稀土对2205双相不锈钢组织及力学性能的影响 [C], 刘晓; Liu Xiao; 马利飞; Ma Lifei; Li Yungang; 李运刚
5.2205双相不锈钢焊接接头组织及纳米压痕性能研究 [C], 杨莉; 戴军; 张尧成
以上内容为文献基本信息，获取文献全文请下载
超级双相不锈钢中δ相力学性能的纳米压痕表征